Characterization of LDPE and LDPE/EVA blends
crosslinked by electron beam irradiation and foamed
with chemical foaming agent
Abstract In this work, low density polyethylene and its
blend with poly (ethylene vinyl acetate) (LDPE/EVA) (80/
20) were mixed with different concentration of Azodicarbonamide
(ACA) as a foaming agent. The specimens were
crosslinked by electron beam irradiation in presence of 1,6-
Hexandiol diacrylate (HDDA). The foam structure was
obtained by heating the crosslinked sheets at 225 °C. The
effect of ACA content and irradiation dose on the gel
percent, tensile strength, cell density, and thermal stabilities
was investigated. The results showed clearly that the
increasing of ACA content reduces the stress and strain at
break and increase the gel content. On the other hand, the
foaming degree increases with increasing the ACA content
and decreases with increasing irradiation dose.
crosslinked by electron beam irradiation and foamed
with chemical foaming agent
Abstract In this work, low density polyethylene and its
blend with poly (ethylene vinyl acetate) (LDPE/EVA) (80/
20) were mixed with different concentration of Azodicarbonamide
(ACA) as a foaming agent. The specimens were
crosslinked by electron beam irradiation in presence of 1,6-
Hexandiol diacrylate (HDDA). The foam structure was
obtained by heating the crosslinked sheets at 225 °C. The
effect of ACA content and irradiation dose on the gel
percent, tensile strength, cell density, and thermal stabilities
was investigated. The results showed clearly that the
increasing of ACA content reduces the stress and strain at
break and increase the gel content. On the other hand, the
foaming degree increases with increasing the ACA content
and decreases with increasing irradiation dose.
这个只是说这机器有什么特点
LDPE 和LDPE/EVA的描述在电子梁照射旁边混合crosslinked，起泡沫化学制品使在这工作里抽象的代理人起泡沫， 低的密度聚乙烯和它的混合物用 poly(乙烯乙烯树脂乙酸盐)(LDPE/EVA)(80 / 20)被与Azodicarbonamide(ACA)的不同的集中混合作为一位起泡沫的代理人。 样品crosslinked 以电子梁照射在1，6-Hexandiol diacrylate(HDDA)的存在。 泡沫结构通过在225癈加热crosslinked床单被获得。 在那些凝胶上影响的ACA 内容和照射剂量百分之，抗拉力量，细胞密度和热稳定性被调查。 结果清楚显示ACA 内容的增加降低压力并且尽力拉休息并且增加 凝胶内容。 另一方面，起泡沫的度用增加ACA 内容增加并且随照射剂量的增加而减少。